Good dielectric performance and broadband dielectric polarization in Ag,Nb co-doped TiO2

Due to the demand of miniaturization and integration for ceramic capacitors in electronic components market, TiO₂-based ceramics with colossal permittivity has become a research hotspot in recent years. In this work, we report that Ag⁺/Nb⁵⁺ co-doped (Ag_1/4Nb_3/4)_xTi_1−xO₂ (ANTOx) ceramics with colossal permittivity over a wide frequency and temperature range were successfully prepared by a traditional solid–state method. Notably, compositions of ANTO0.005 and ANTO0.01 respectively exhibit both low dielectric loss (0.040 and 0.050 at 1 kHz), high dielectric permittivity (9.2 × 10³ and 1.6 × 10⁴ at 1 kHz), and good thermal stability, which satisfy the requirements for the temperature range of application of X9R and X8R ceramic capacitors, respectively. The origin of the dielectric behavior was attributed to five dielectric relaxation phenomena, i.e., localized carriers' hopping, electron–pinned defect–dipoles, interfacial polarization, and oxygen vacancies ionization and diffusion, as suggested by dielectric temperature spectra and valence state analysis via XPS; wherein, electron-pinned defect–dipoles and internal barrier layer capacitance are believed to be the main causes for the giant dielectric permittivity in ANTOx ceramics.     

Detection of crowdedness in bus compartments based on ResNet algorithm and video images

Multimedia Tools and Applications - The crowding in bus is an important factor affecting passenger satisfaction and bus dispatching level. However, how to use video images to detect crowding...     

A multilayer recognition model for twitter user geolocation

Wireless Networks - Geolocation is important for many emerging applications such as disaster management and recommendation system. In this paper, we propose a multilayer recognition model (MRM) to...     

成分配比对稀土钨电极材料组织及力学性能影响

通过固液掺杂、等静压压制、中频烧结的方法，制备了不同的氧化镧、氧化钇、氧化锆三元掺杂成分比例的钨电极材料烧结棒材，探究了不同成分配比对样品显微组织、第二相粒子分布以及宏观力学性能的影响。结果表明，氧化镧、氧化钇、氧化锆三元复合添加能够有效改善第二相粒子在钨基体中的分布形态，降低第二相在晶界的过度富集，提高钨电极材料的综合力学性能。并且当添加成分镧、钇、锆质量比为3:1:1时，材料具有最好的综合力学性能，致密度可达96.04%，显微硬度可达549.37HV0.3，抗压强度可达3785MPa，原因是此配比下第二相粒子最为细小均匀，弥散程度最高，对基体晶粒的细化作用最好，该配比下钨基体平均晶粒尺寸达到10.3μm。     

Effect of high hydrostatic pressure pretreatment on flavour and physicochemical properties of freeze-dried carambola slices

Ripe carambolas are hard to store and transport, while freeze-dried ones are easy to store. However, its long production time leads to higher costs. This study shows that high hydrostatic pressure (HHP) treatment could shorten the freeze-drying time of carambola slices. After HHP treatment (25–250 MPa), the drying time of the fresh sample can be shortened by 33.3–44.4% and the distribution of water and pigment in tissues is much uniform. With the increment of the pressure, 2,2-diphenyl-1-picrylhydrazyl (DPPH) and hydroxyl radical scavenging rate are increased. At 250 MPa, the total phenolic content (TPC) increased from 11.34 to 13.36 mg GAE g⁻¹, and the total flavonoid content (TFC) of the control sample was increased from 10.77 to 12.73 mg RE g⁻¹. Compared with the untreated sample, HHP treatment can enhance the flavour and shorten the freeze-drying time. This work guides the application of HHP technology for drying food processing.     

Theoretical investigation of intrinsic point defects and the oxygen migration behavior in rare earth hafnates

In this work, the composition-dependent point defect types and formation energies of RE₂Hf₂O₇ (RE = La, Ce, Pr, Nd, Pm, Sm, Eu and Gd) as well as the oxygen diffusion behavior are systematically investigated by first-principles calculations. The possible defect reactions and dominant defect complexes under stoichiometric and non-stoichiometric conditions are revealed. It is found that O Frenkel pairs are the predominant defect in stoichiometric pyrochlore hafnates. Hf-RE cation anti-site defects, accompanied by RE vacancies and/or oxygen interstitials, are stable in the non-stoichiometric case of HfO₂ excess. On the other hand, RE-Hf anti-site defects together with oxygen vacancies and/or RE interstitials are preferable in the case of RE₂O₃ excess. The energy barriers for the migration along the V_O48f - V_O48f pathway of pyrochlore hafnates were calculated to be between 0.81 eV and 0.89 eV. Based on these results, a defect engineering strategy is proposed and the pyrochlore hafnates investigated here are predicted to exhibit potential oxygen ionic conductivity.     

MOF衍生的高选择性加氢芳香硝基化合物的石墨碳包覆镍催化剂

针对芳香硝基化合物的催化选择性加氢反应，开发可替代贵金属催化剂的低成本、高效非贵金属催化剂，对于芳香胺类化合物的绿色生产具有重要意义。利用简易、可规模化的制备方法，以镍—2,5-吡啶二羧酸金属有机框架为前驱体，热解制备了氮掺杂石墨碳包覆镍纳米催化材料（Ni@CN）。采用X射线衍射、扫描电镜、透射电镜、元素分析、N2吸脱附等检测手段对Ni@CN的物化性质进行了表征，并对其催化性能进行了评价。结果表明，Ni@CN可在温和条件下（85℃，1.0 MPa H2)高效加氢含取代官能团的芳香硝基化合物生成对应的芳香胺类化合物。对比试验表明，镍纳米颗粒是Ni@CN的加氢活性中心，而石墨碳壳的存在有利于优先吸附硝基官能团。此外，进一步考察了Ni@CN的循环使用性能以及抗硫化物中毒的特性。